Vinyl Asylum

Welcome Licorice Pizza (LP) lovers! Setup guides and Vinyl FAQ.

Use this form to submit comments directly to the Asylum moderators for this forum. We're particularly interested in truly outstanding posts that might be added to our FAQs.
You may also use this form to provide feedback or to call attention to messages that may be in violation of our content rules.

You must login to use this feature.

Inmate Login

By default, logging in will set a session cookie that disappears when you close your browser. Clicking on the 'Remember my Moniker & Password' below will cause a permanent 'Login Cookie' to be set.

Moniker/Username: The Name that you picked or by default, your email. Forgot Moniker?	Examples "Rapper", "Bob W", "joe@aol.com".
Password:	Forgot Password?
	Remember my Moniker & Password ( What's this?)

If you don't have an Asylum Account, you can create one by clicking Here.

Our privacy policy can be reviewed by clicking Here.

Inmate Comments

From:
Your Email:
Subject:

Message Comments

Original Message

Only if you exceed the yield stress.

Posted by Mark Kelly on October 27, 2006 at 16:39:40:
Vinyl as used in records is used above its glass / rubber transition point so it acts as a rubber. It's very difficult to push a rubber beyond its compressive yield stress because it acts basically like a condensed fluid.
When I get time I will try to get together more information on elastic/plastic deformation and creep strain behaviour in vinyl.
Mark Kelly